Paint UHS transparent MF 7447
Index: MF 7447
Paint transparent (1 l), colour: transparent, UHS, proportions: 2:1, application type: gun
Acrylic Clear Coat SPARK 07 UHS 2:1
Acrylic Clear Coat SPARK 07 UHS 2:1
Variant
| Colour | Material | Capacity |
|---|---|---|
| Clear | Acrylic | 1L |
High-quality 2K acrylic clear coat with low volatile compound content. Designed for full body repairs. Provides a deep gloss to the surface and enhances the depth of the base colour. It is characterised by high durability and excellent UV protection.
Advantages
- Very high solid content >55%.
- Excellent surface appearance.
- Easy application.
- Very good spray mist absorption.
- Excellent flow.
Substrates
Clear acrylic coats can be applied to:
- Base coats.
- Old finishes in good condition after matting and degreasing.
Matting:
- Sandpaper with grit 600÷800 (for wet matting).
- Sandpaper with grit 360÷500 (for machine matting).
Degrease
Mixing ratio
2 : 1 + 0%
Spray viscosity
17 ÷ 19s / 20°C
Pot life
3.5 h/20°C (standard hardener)
2 h/20°C (standard hardener)
1.5÷2×1 layers
HVLP / RP
ø1.3 ÷ 1.4 mm
1.2 ÷ 1.4mm
Between layers:
approximately 5-10 minutes
Before baking:
approximately 10 minutes
Curing time
40 min. / 20°C
10 min. / 60°C (standard hardener)
Description
Acrylic Clear Coat SPARK 07 UHS 2:1
Acrylic Clear Coat SPARK 07 UHS 2:1
Variant
| Colour | Material | Capacity |
|---|---|---|
| Clear | Acrylic | 1L |
High-quality 2K acrylic clear coat with low volatile compound content. Designed for full body repairs. Provides a deep gloss to the surface and enhances the depth of the base colour. It is characterised by high durability and excellent UV protection.
Advantages
- Very high solid content >55%.
- Excellent surface appearance.
- Easy application.
- Very good spray mist absorption.
- Excellent flow.
Substrates
Clear acrylic coats can be applied to:
- Base coats.
- Old finishes in good condition after matting and degreasing.
Matting:
- Sandpaper with grit 600÷800 (for wet matting).
- Sandpaper with grit 360÷500 (for machine matting).
Degrease
Mixing ratio
2 : 1 + 0%
Spray viscosity
17 ÷ 19s / 20°C
Pot life
3.5 h/20°C (standard hardener)
2 h/20°C (standard hardener)
1.5÷2×1 layers
HVLP / RP
ø1.3 ÷ 1.4 mm
1.2 ÷ 1.4mm
Between layers:
approximately 5-10 minutes
Before baking:
approximately 10 minutes